For purification of gas streams from CO, NOx, SOx, HCL, HF, VOC, dioxins, polydisperse dust particles with temperature up to 1000 0C and concentration of solid particles up to 20 g/m3.
Price on request
Applications
Smelting and roasting furnaces, drying drums, reactors, furnaces, etc.
Granular ceramic filter elements are made of coarse-grained silicon carbide or aluminium oxide (substrate) with a thin selective layer - membrane - applied on the outer surface. The pore size of the substrate and membrane is selected based on the specific task, based on the data on the disperse composition of the separated particles, the required aerodynamic resistance and the efficiency of gas purification.
Parameter | Unit of measurement | Value | |
Filtration rate | μm | ≤ 0,3 | |
Substrate porosity | % | 38 | |
Material density |
g/cm2 | 1,85 | |
Bending strength (annular compression) | MPa | ≥ 20 | |
Maximum temperature resistance | 0С | 1000 | |
Filtration of hot gases in an oxidising environment | 0С | 750 | |
Filtration of hot gases in a reducing environment | 0С | 600 | |
Coefficient of thermal expansion (25-1000 ℃) | К | 5,6 10-6 | |
Thermal conductivity (200 ℃) | W/m * K | 2,5 | |
Filtration area |
m2 | 0,175 | |
Outer diameter | mm | 60 | |
Internal diameter | mm | 40 | |
Length | mm | 1000 | |
Weight | kg | 3 | |